Customized Anodizing Production Line for Aluminum Surface Treatment with Sulfuric Acid Electrolyte Output 900Ton/month

Anodizing Production Line for Aluminum Surface Treatment with Sulfuric Acid Electrolyte

一.Product overview

1.Aluminum anodizing involves placing aluminum and its alloys in a corresponding electrolyte (such as sulfuric acid, chromic acid, oxalic acid, etc.) as an anode, and conducting electrolysis under specific conditions and applied current.

2.The oxidation of aluminum or its alloys on the anode forms a thin layer of aluminum oxide on the surface, with a thickness of 5-30 microns. The hard anodic oxide film can reach 25-150 microns.

3.After anodizing, aluminum or its alloys have improved their hardness and wear resistance, reaching up to 250-500 kg/square millimeter. They have good heat resistance, a hard anodized film melting point of up to 2320K, excellent insulation properties, and a breakdown voltage resistance of up to 2000V, enhancing their corrosion resistance. They do not corrode after thousands of hours in ω=0.03NaCl salt spray.

二. Design Condition

三.Process Tank

四.Treatment Process:

1. Degreasing
   (1) 6jig(rack)/ tank x 1 tank=6jig(rack)
   (2) treatment time: 2-5min
2. Alkaline Etching
   (1) 6jig(rack) / tank x 2 tank=12jig(rack)
   (2) treatment time: 3-15min
3. Neutralization
   (1) 6jig(rack) / tank x 1 tank=6jig(rack)
   (2) treatment time: 1-5min
4. Anodizing
   (1) 2 jig(rack)/tank x 4tanks = 8jig(rack)
   (2) Current density: 130A/m²
   (3) Process time: 30min
   (4) Unprocess time: 10min
   (5) Total time 30+10=40min

(6) Average anodizing layer : 0.3*1.3*30*0.77 =10.81um

5. Colour 1

1) Clour process: Mix Salts

2) Quantity:2 jig(rack)/tank x 1tanks = 2jig(rack)

3) Current density: 70A

4) Process time: 2-8min

6. Sealing
1) Sealing menthod: Sealing at Medium or Normal Temperature
2) Quantity:6jig(rack)/tank x 1 tank
3) Process time 10-15min

五. Design Parameter and Setting

1. Anodizing treatment area:
1) Each anodizing process tank need 40min ,where total jig(rack)/year:​

( 2 rack x 4 tank x 60min/h) ÷40min x600 hour =7200jig(rack)

2) Design 50m²^/jig(rack) . Where every tank is 100m²
3) Area treatment/year : 7200jig(rack)x 50m² /jig =360000m²

2. Anodizing treatment weight:
Monthly output : 360000m²÷350m²/T*0.9=925T≧900T

3. Power consumption:
1) Anodising Tank:100m²/tank* 130A/ m²÷0.9=14444A/tank

Power Rectifier : 15000A =4unit
2) Clouring tank: 100㎡/tank×70A/m²÷0.9 = 7777A/tank

Colour Rectifier : 8000A =2unit

六. Process Chat

MEI-AL Technology has been committed to serve the aluminum profile surface treatment industry with its strong technical force, excellent production and processing, scientific management methods and excellent management style. Mei-al main production: anodizing, coloring, electrophoresis production line, products have special high-power silicon control rectifier, high-power high-frequency switching power equipment, electrophoresis workshop pure water equipment(RO machines), refining equipment, electrophoretic paint recovery equipment, electrophoresis curing furnace,loading and unloading machines,1T+1T professional anodizing cranes, anodizing tank temperature control system and production line automatic control system, etc.

In our perpetual effort and support of our partners in the industry,MEI-AL Technology  has obtained outstanding achievements and is still maintaining a rapid development speed.With the operation spirit of “Professional, Concebtration, Integrity, Co-win”, MEI-AL Technology will provide with you excellent products and perfect services, in the rooted concept of Growind Up with You !