Categories | Water Based Hydroxyl Acrylic Resin |
---|---|
Model Number: | WL-153 |
Certification: | ISO9001 |
Place of Origin: | china |
MOQ: | 5000KG |
Payment Terms: | L/C, T/T |
Supply Ability: | 500t/month |
Delivery Time: | 14 work days |
Packaging Details: | 200kg/drum |
Brand Name: | WeiLi Resin® |
Price: | Negotiable |
Appearance: | milky white emulsion |
Non-Volatile Matter: | 42±2.0%(120℃/30min) |
PH value: | 7-8 |
Hydroxyl Value: | 78mgKOH/g |
Viscosity: | ≤1000mPa.s |
Package: | 200kg |
Company Info. |
Xiamen WangQin Chemical Technology Co., Ltd. |
Verified Supplier |
View Contact Details |
Product List |
Reacted with polyisocyanate, water based hydroxyl acrylic dispersion can produce the same hardness, impact resistance and solvent resistance as solvent based polyurethane coating. PU coating made of WL-153 is recommended to use in topcoat of metal or wood due to its paint film has excellent gloss, the construction method can be brushing, roll coating or spraying. This two component PU resin WL-153 is recommended to be used in place of Bayer A145 due to its similar properties with Bayer A145. |
Gloss(60o)high gloss kind | >90 | Adhesion(grid) | 0 grade |
Surface dry min(23o) | 15min | Adhesion(circle) | 1grade |
Air dry 25o/h | 4h | Water resistance(23o) | 480h |
Baking 65o/min | 65o,30min | Alkaline resistance (25o 0.1N NaOH) | 24h |
Pot life(25o) | 4h | Acid resistance (25o 0.1N H2SO4) | 24h |
Hardness(pencil) | 1H-2H | Gasoline resistance | 24h |
Flexibility/mm | 1grade | Artificial aging resistance | 1000h Loss of gloss 30% |
Impact resistance kg*cm | 50 | Q-sun,1200h | 1grade |
Heat resistance | 105o | Continue 24h | 24h |
Resin | Gloss | Limit film thickness | Surface dry | Air dry | Hardness |
A145 | 90 | 60 | 20mins | 4h | 2H |
WL153 | 88 | 70 | 20mins | 4h | 2H |