Dip Spin Dacromet Finish Radius Thickness Ratio Zn Plate 60~100 Silvery Color

Categories Dacromet Coating
Brand Name: SHISHENG
Model Number: MX6380
Certification: ISO9001
Place of Origin: Changzhou in china
MOQ: 100 Kilograms
Price: Negotiable
Payment Terms: L/C, T/T
Supply Ability: 5 Tons per Day
Delivery Time: Ten days after receipt of advance payment
Packaging Details: Pack A:16kg/ Metal Barrel Pack B:24KG Plastic Barrel Pack C:Based on the amount of B agent A
Color: Silvery
PH: 3.8-5.2
Specific gravity: 1.30±0.05
Viscosity: 20~50s(Spray Coating) 65~80S(Dip-Spin Coating)
Cr6+: ≥25g/L
  • Haven't found right suppliers
  • Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
  • And this service is free of charge.
  • we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!
  • Submit Buying Request
    • Product Details
    • Company Profile

    Dip Spin Dacromet Finish Radius Thickness Ratio Zn Plate 60~100 Silvery Color

    Dip Spin Dacromet Finish Radius Thickness Ratio Zn Plate 60~100 Silvery Color


    Zinc flake coatings are non-electrolytically applied coatings, which provide good protection against corrosion. These coatings consist of a mixture of zinc and aluminium flakes, which are bonded together by an inorganic matrix.

    The specifications for zinc flake coatings are defined in international standard ISO 10683 and also in European standard EN 13858. ISO 10683 sets out the requirements for zinc flake coatings for threaded fasteners and EN 13858 describes the requirements for zinc flake coatings for fasteners with no thread and for other parts as well. There are three groups of zinc flake coatings:


    Metal Dacromet Coating Introduction


    Dacromet process is the most representative of today''s international metal surface treatment of high-tech, widely used in the world''s industrialized countries. Based on the author''s first-hand information in design and production, this paper describes in detail the characteristics of Dacromet coating process, the choice of equipment and Dacromet liquid, and the application of Dacromet coating process in China.


    Composition/information on ingredients


    MX6380 is made up of three packs: A,B and C;

    Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and ethylene glycol. The radius-thickness ratio of Zn plate is 60~100.

    Pack B: It is the solvent of the coating colored in orange-red and in water solution, which contain the Cr6+.

    Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.


    Coating Process


    3.1 Mix Ratio

    Pack A:16.0 kg

    Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)

    Pack C:0-50 g (according to different viscosity demand )


    3.2


    Mixture Method

    Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.

    3.2.2

    Add B to the stirring A slowly. At the moment ,the barrel temperature will go up,when it reaches 35℃, startup refrigerating device to keep the barrel temperature constant at 35℃.

    3.2.3


    Stir the mixture about 1~2 hours fast after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30℃, otherwise C will not be dissolved sufficiently .)Then stir 12 hours continuously.


    3.2.4


    The coating should be filtrated by 80~100 mesh stainless steel screen before pouring into dip barrel.


    3.2.5


    Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2℃.(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.


    3.2.6


    Test density,PH,Temperature,Viscosity and Cr6+ content of coating every 8 hours if operate continuously.


    4. Technical data


    No.ItemData
    1PH3.8-5.2
    2Cr6+≥25g/L
    3Specific gravity1.30±0.05
    4Viscosity20~60s(Spray Coating) ; 60~90S(Dip-Spin Coating) . 20℃ Zahn 2# cup
    5Operating temperature22±2℃

    5. Mix Diagram


    Caution: Temperature should be controlled in above operation.


    6. Coating Process



    6.1 Degreasing

    The workpiece should be degreased if there is oil on the surface. There are three processing methods:

    1.High temperature

    2.Neutral water-base degreasing agent

    3.Organic solvent such as methylene chloride.


    6.2 Derusting

    The workpiece can not be coated if there is rust or burr on the surface.The best processing method is shot blasting. The corrosion resistance of coating will be effected if acid cleaning adopted.


    6.3 Coating

    The workpiece afer degreasing and shot blasting should be coated through Dip-Spin coating or Spraying Coating.


    6.4 Pre-heating

    The workpiece after coated should be Pre-heated as soon as possible at 80~150℃ for 8~15 mins to evaporate. ( according to heat absorption of workpiece.)


    6.5 Curing

    The workpiece after pre-heating should be cured at 300-340℃ for 20-40 mins. ( according to heat absorption of workpiece.)


    7. Attentions


    Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.

    Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .

    It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature,viscosity and spinning process shoud be controlled well when coating.

    The viscosity will be different if coating method is different. Choose low data if spray coating,and choose high data if dip spin coating.


    8. Packing


    Pack A:16kg/ Metal BarrelPack B:24KG Plastic BarrelPack C:5.0kg metal barrel

    9. Quality guarantee period

    Before compound 6 months at 20℃

    After compound 40 days at 20℃ ( It can be recycled if adding fresh coating continuously. )

    It should be stored under 20℃ if not in use.

    Product Tags:

    dacromet plating

      

    anti corrosion paint

      
    Quality Dip Spin Dacromet Finish Radius Thickness Ratio Zn Plate 60~100 Silvery Color for sale
    Send your message to this supplier
     
    *From:
    *To: Changzhou Shisheng Machineries Co.,Ltd.
    *Subject:
    *Message:
    Characters Remaining: (0/3000)
     
    Inquiry Cart 0

    Friendly Links: www.everychina.com

    Home| Products| Suppliers| Quality Suppliers| Site Map |About Us |Contact Us |Help |关于我们 |联系我们

    Copyright © 2009 - 2024 wneducation.com. All rights reserved.