Composition: from epoxy resin, anti-rust pigments by grinding, add liquid coal
tar pitch, additives and organic solvents deployment into Group A,
by the polyamide solution with into the B copies.
Characteristics: film with excellent adhesion, salt water and strong resistance to
chemical media can be resistant to some of the alkali solution, a
good corrosion protection.
Purpose: for underwater and underground facilities and equipment, such as
oil pipelines, underground sewage pipes and storage tanks, etc.,
for heavy machinery, anti-corrosion oil.
g / cm 3
Group A 1.10 ~ 1.30
B 0.85 ~ 1.00
wet film thickness
dry film thickness
kg / . Road
drying time, surface dry
h (232 ℃)
h (232 ℃)
Group: Group B (by weight)
maturity of the period
mixed use of time
Overcoating interval: shortest 24h, up to 72h.
Suggested painting number: 2-3 Road.
With matching paint: H06-4 epoxy zinc-rich primer, H52-80 Anticorrosion Epoxy Asphalt
lead powder paint, H06-2 colored chlorinated rubber primer.
Surface treatment: a zinc-rich primer Epoxy primer or aluminum, should be divisible
by dirt on the film, with oxide of steel should be blast to Sa 2 or
Sa 2.5, scale should be hand-polished steel to St 3 class.
Substrate temperature: than 3above the dew point temperature below 5not painting.
Coating method: air spray, brush.
Thinner: X-7 epoxy paint thinner.
Valid: tentative six months, extended by the inspection shall be approved
Safety and protection: in the construction of a well-ventilated and dry environment, the
construction work were to wear protective equipment.